title:
|
||
"Polyoxometalate Incorporation and Effects on Proton Transport in Hydrogel
|
||
Polymers"
|
||
date: 2020-08-07
|
||
cardImage: library
|
||
draft: false
|
||
featured: true
|
||
keywords:
|
||
- bioremediation
|
||
- polyoxometalate
|
||
- hydrogel polymers
|
||
- proton transport
|
||
- chemical engineering
|
||
medium: thesis
|
||
people:
|
||
- Thomas A. Christensen II
|
||
link: "https://www.proquest.com/dissertations-theses/polyoxometalate-incorporation-effects-on-proton/docview/2502214356/se-2"
|
||
journal: "University of Idaho"
|
||
location: "Moscow, Idaho"
|
||
---
|
||
|
||
Polyoxometalate clusters embedded into hydrogel biobeads may be able to solve
|
||
the challenges posed by free proton generation during remediation of
|
||
trichloroethylene by acting as buffers and reducing protons to hydrogen gas. In
|
||
this thesis, the challenges posed by systems that contain both diffusion and
|
||
reaction processes for protons are considered mathematically, and a computer
|
||
simulation to was developed to prove the relationship between diaphragm cell lag
|
||
period and reactive capabilities of membranes. Two polyoxometalate compounds,
|
||
sodium decavanadate and alumina sulfate, were successfully incorporated into a
|
||
poly(vinyl alcohol) hydrogel membrane, and the diffusivity changes associated
|
||
with each compound was determined. It was found that the diffusivity of protons
|
||
through an unmodified 10% w/v poly(vinyl alcohol) membrane was 1.76 ×
|
||
10{{< sup -5 >}} cm{{< sup 2 >}} s{{< sup -1 >}}, the diffusivity through a
|
||
10%/2% w/w/v poly(vinyl alcohol)/sodium decavanadate membrane was 3.10 ×
|
||
10{{< sup -6 >}} cm{{< sup 2 >}} s{{< sup -1 >}}, and the diffusivity through a
|
||
10%/2% w/w/v poly(vinyl alcohol)/alumina sulfate membrane was 3.32 ×
|
||
10{{< sup -7 >}} cm{{< sup 2 >}} s{{< sup -1 >}}. Through analysis of the
|
||
diaphragm cell lag period, it was found the incorporation of sodium decavanadate
|
||
did not increase the reactivity of a poly(vinyl alcohol) hydrogel, and
|
||
incorporation of alumina sulfate lowered the reactivity. These results indicate
|
||
that polyoxometalate integration into hydrogel membranes is feasible, but does
|
||
not provide any advantage to a bioremediation scenario.
|